日本变形铝及铝合金化学成份

作者：bearingpower        发表时间：2010-12-12

日本变形铝及铝合金化学成份关键字：铝 合金牌号化 学 成 分，wt%杂质Al wt% SiFeCuMnMgCrNiZnGaV其他Ti单个总计A11990.0060.0060.0060.0020.0060.0060.0050.0005?0.0020.002?99.99A10950.0300.0400.0100.0100.0100.010?0.0050.005?99.95A10900.070.070.020.010.010.030.030.05?0.010.01?99.90A10800.150.150.030.020.020.030.030.05?0.030.02?99.80A10700.200.250.040.030.030.04?0.05?0.030.02?99.70A10500.250.400.050.050.050.05?0.05?0.030.03?99.50A13500.100.400.050.01?0.01?0.050.03?B0.05 (V+Ti) 0.02?0.030.1099.50A10300.350.60.100.050.050.10?0.05?0.030.03?99.30A1200（Si+Fe）0.950.050.05?0.10①0.050.050.1599.00A1100(Si+Fe)0.950.05-0.200.05?0.100.050.1599.00A30030.60.70.20-0.501.0-1.60.100.050.15余量A30040.300.70.251.0-1.50.8-1.30.25?0.05?0.15余量A50050.300.70.200.200.50-1.10.10?0.250.050.15余量A50520.250.400.100.102.2-2.80.15-0.35?0.100.050.15余量A50560.300.400.100.05-0.204.5-5.60.05-0.20?0.100.050.15余量A54540.250.400.100.50-1.02.4-3.00.05-0.20?0.25?0.200.050.15余量A50830.400.400.100.40-1.04.0-4.90.05-0.250.25?0.150.050.15余量A60630.20-0.60.350.100.100.45-0.90.10?0.10?0.100.050.15余量A60610.4-0.80.70.15-0.400.150.8-1.20.04-0.35?0.25?0.150.050.15余量A21170.80.72.2-3.00.200.20-0.500.10?0.25?0.050.15余量A20170.20-0.80.73.5-4.50.40-1.00.40-0.80.10?0.25②0.150.050.15余量A20240.500.503.8-4.90.30-0.91.2-1.80.10?0.25②0.150.050.15余量A20140.50-1.20.73.9-5.00.4-1.20.20-0.80.10?0.25②0.150.050.15余量A26180.15-0.250.9-1.41.8-2.70.251.2-1.8?0.8-1.40.15(Zr+Ti) 0.250.200.050.15余量A70750.400.501.2-2.00.302.1-2.90.18-0.285.1-6.1②0.200.050.150.15余量日本特有合金合金牌号化 学 成 分，wt%杂质Alwt%SiFeCuMnMgCrNiZnGaV其他Ti单个总计2N01 ③0.50-1.30.6-1.51.5-2.50.201.2-1.8?0.6-1.40.20?0.20